Why does the amount of Co and WC particle size affect the thickness of the heat affected layer?
It is thought that when Co is in large quantities the fusing point is lowered, which increases the amount that melts and thickening the damaged layer.
It is also thought that when WC particle size is small, the material becomes easier to melt due to the volume effect, which thickens the damaged layer.
Q&A in the same category in this question
-
Why is there a 50% change in volume?
Carbide is a material made by compacting powder during sintering, and there are some gaps inside the carbide where air and particles collide.
Through sintering, the cobalt liquefies, and a 50% reduction in volume occurs when tungsten particles are attracted due to the capillary phenomenon. The contacting surfaces of different powdered particles try to mix and homogenize, inducing the atoms to move in an attempt to create new compounds. -
What causes cemented carbide to crack?
Compared to metal materials, cemented carbide materials have a different thermal expansion coefficient. For this reason, cracks may occur in shrink/cooling-fitted products when the operating temperature is significantly higher (lower) than the designed value. When using cemented carbides with high hardness, problems such as cracking may occur by high impact, so the required fracture toughness value should also be carefully considered.
-
What is the difference between cemented carbide and HSS?
Cemented carbide is an alloy with high hardness, heat resistance and strength. HSS, on the other hand, generally has relatively lower strength and heat resistance, but has higher impact resistance.
As their raw materials and manufacturing methods differ, there is a significant difference in costs between the two materials.
Selecting the suitable material is recommended though considering the application and the timing of replacement after installation.
-
Catalog
We will provide high value-added cemented carbide with the achievements and know-how cultivated so far.
Download -
Consultation and Inquiry
We solve your problems by providing integrated solutions from material selection/development to precision machining and provision of finished products.
Contact us -
FAQ
We have posted the contents of many inquiries from customers in the past.
Click for details